kitchen sink shapes machine Using argon arc welding wire to repair mold steel technology Zhisheng automated welding equipment
Using argon arc welding wire to repair mold steel technology
Wire material: SKD11 SKD61 NAK80 8407 H13 718 738 888 P20 420 S136 2344 2316 2083 PDS 2311 PX5 2711 PX88 Beryllium copper Argon robotic welding machinecopper Yellow card repair mold robotic welding machinematerials. Wire diameter specifications: 0.9, 1.0, 1.2, 1.6, 2.0, 2.4, 3.2 * 1000mm wire use: SKD11 > 1.0 ~ 3.2mm HRC 56~58 Welding cold working steel, metal stamping dies, cutting dies, cutting tools, forming dies, workpieces Hard face made of argon robotic welding machinerods with high hardness, wear resistance and high toughness, robotic welding machinerepair Before warming and preheating, it is easy to produce cracks. SKD61 > 0.9 ~ 3.2mm HRC 40~43 Welding zinc, aluminum die casting, good heat resistance and crack resistance, hot stamping die, aluminum/copper hot forging die, aluminum/copper die casting die, heat resistant , wear resistance, crack resistance. Generally, hot-pressed molds are often cracked. Most of them are caused by thermal stress, and are also caused by surface oxidation or corrosion of die-casting materials. Heat treatment is adjusted to an appropriate hardness to improve its service life. Hardness is too low or too high. Be applicable. 8407-H13 > 0.9 to 3.2mm HRC 43~46 Dies for non-ferrous alloys and copper alloys made of zinc, aluminum, tin, etc. can be used as hot forging or stamping dies. With high toughness, wear resistance and good thermal erosion resistance, high temperature softening, high temperature fatigue resistance, can be used as heat treatment for punch, reamer, rolling knife, grooving knife, scissors... When it is necessary to prevent decarburization, the hardness of the hot tool steel after robotic welding machineis too high and it also breaks. 888T > 1.2~1.6mm HB~300 High-hardness steel joints, hard-surfaced bases, and cracked welds. High-strength welds, high nickel-chromium alloy composition, specializing in the prevention of cracking the bottom of the welding, filling the bottom, strong pull, and repair the cracking of steel robotic welding machinereconstruction. 718 > 0.9 ~ 2.4mm HRC 28~30 Mold steel for plastic products such as large home appliances, toys, communications, electronics, and sports equipment. Plastic injection molds, heat-resistant molds, corrosion-resistant molds, good machinability, erodibility, excellent surface gloss after grinding, and long service life. The preheating temperature is 250~300°C and the post-heating temperature is 400~500°C. When using multi-layer welding, the robotic welding machinemethod is used for backward welding, which is less likely to cause defects such as poor fusion and pinholes. 738 > 0.9 ~ 2.4mm HRC 32~35 Translucent and surface-glossy plastic product mold steel, large-scale mold, product shape complex and high precision plastic mold steel. Plastic injection molds, heat-resistant molds, corrosion-resistant molds, and good corrosion resistance, with excellent processing properties, easy to cut light and erosion, toughness and good wear resistance. Preheating temperature 250 ~ 300 °C after the heat temperature 400 ~ 500 °C, for multi-layer welding, using the back robotic welding machinemethod, less prone to fusion defects and pinholes and other defects. P20Ni > 0.9 ~ 2.4mm HRC 30~34 Plastic mold, heat-resistant mold (cast copper mold). Designed with alloy components with low sensitivity to robotic welding machinecracks, containing about 1% nickel, suitable for PA, POM, PS, PE, PP, ABS plastics, with good light, no pores, cracks after welding, polished after a good Smooth finish, after vacuum degassing, after forging, pre-hard to HRC 33 degrees, uniform hardness distribution on the section, die life of 300,000 or more. The preheating temperature is 250-300°C and the post-heating temperature is 400-500°C. When performing multi-layer welding, the robotic welding machinemethod is used for backward welding, which is less likely to cause defects such as poor fusion and pinholes. NAK- 80 > 0.9 ~ 1.6mm HRC 38~42 Plastic injection mold, mirror steel. High hardness, excellent mirror effect, good electric discharge machining, excellent robotic welding machineperformance, smooth and mirror-like after polishing, it is the most advanced and best mold steel in the world, easy to cut elements added, easy cutting, high strength, toughness and resistance Grinding without deformation characteristics, suitable for a variety of transparent plastic products die steel. Preheating temperature 300 ~ 400 °C after the heat temperature 450 ~ 550 °C, when multi-layer welding, using the back-up robotic welding machinemethod, less prone to fusion defects and pinholes and other defects. S-136 > 0.9~1.6mm HB~400 plastic injection mold, good corrosion resistance and permeability. High purity, high specularity, good light, excellent rust and acid resistance, less heat treatment, suitable for PVC, PP, EP, PC, PMMA plastics, corrosion-resistant and easy to process modules and fixtures, super mirror corrosion resistance Precision molds, such as rubber molds, camera parts, lenses, cases, etc. 200T (Emperor S-2)> 0.9~2.4mm HB~200 iron mold, shoe mold, mild steel welding, easy engraving, S45C, S55C steel repair. Yellow card electrode repair texture fine, soft, easy processing, there will be no porosity, generally yellow robotic welding machineelectrode on the market, although the price is cheap, but the hardness is too high after repair, not easy to eclipse flowers and prone to stomata (welcome to call sampling) . The preheating temperature is 200~250°C and the hot temperature is 350~450°C. BeCu (bismuth copper) > 0.9~1.6mm HB~300 high thermal conductivity copper alloy mold material, the main additive element is yttrium, which is suitable for plastic injection molding mold inner insert, core, die-casting punch, hot runner cooling system, heat conduction Mouth, blow mold, integral cavity, wear plate, etc. Tungsten-copper materials are used in resistance welding, EDM, electronic packaging, and precision mechanical equipment. CUS (argon robotic welding machinecopper) > 0.9~2.4mm HB~200 This robotic welding machinebranch is widely used for robotic welding machinerepair of electrolysis sheets, copper alloys, steel, bronze, pig iron, and general copper parts. Good mechanical properties, can be used for robotic welding machinerepair of copper alloys, but also robotic welding machinesteel and pig iron, iron joining. OH1-1G (oil steel) > 1.0~1.6mm HRC 52~57 Blanking Die, Gauge, Die, Piercing Punching, Widely Used in Hardware Cold Stamping, Hand Embossing Dies, General Purpose Special Tool Steel, Wear Resistant, Oil Cooled . Cr steel > 1.0~1.6mm HRC 55~57 Blanking die, cold working die, cold die, punch, high hardness, high tenacity, and good wire cutability. Warm up and preheat before welding, and do post-robotic welding machineafter welding.
As a entrepreneur, being trapped in a company under multiple quality problems never appealed to Jiangmen Zhisheng Automation Welding Equipment Co., Ltd..
is a kitchen sink shapes machine sink welding press machine provided by Jiangmen Zhisheng Automation Welding Equipment Co., Ltd. which is a leading manufacturer in China. For more information, visit Zhisheng automated welding equipment.
Jiangmen Zhisheng Automation Welding Equipment Co., Ltd. has been making a name for itself as a producer of some of the finest in the China, and it has been singing its praises for some time.
It is never too late to have a new mindset and to get things moving in the right direction. Choose Jiangmen Zhisheng Automation Welding Equipment Co., Ltd. to be your quality provider.
The more people who do a certain thing, the more likely others are to do it as well. When Zhisheng automated welding equipment can demonstrate their popularity or satisfaction across a wide customer base, other consumers are more likely to buy in as well.
Media contact Company Name: Jiangmen zhisheng automatic welding equipment co., LTD. Address: Hulu foot on the 2nd, Dazei Town, Xinhui District, Jiangmen City,China E-mail:
[email protected] Website: http://www.jgdzs-welding.com/